Kādi ir parasti izmantotie pamatmateriāli loka metinātām caurulēm?
Common base materials for arc welded pipes include carbon steel (such as Q235, API 5L), low alloy steel (such as 16Mn), stainless steel (such as 304, 316) and heat-resistant steel (such as P91). Carbon steel has low cost and moderate strength, and is widely used in construction and water pipelines. Low alloy steel (such as X70) is used for high-pressure oil and gas transportation. Stainless steel is corrosion-resistant and suitable for the chemical and food industries. Heat-resistant steel is used in high-temperature environments, such as power station boiler tubes. Different materials need to match corresponding welding materials and processes.
Kā izvēlēties pareizo metināto caurules materiālu atbilstoši lietojumprogrammas scenārijam?
Metināto cauruļu materiālu izvēlei jāapsver barotnes, darba temperatūras, spiediena un izmaksu . oglekļa tērauda korozivitāte var izmantot ūdensvadiem, bet nerūsējošā tērauda vai anti-korozijas pārklājums ir nepieciešams jūras ūdens videi . Eļļa un gāzes cauruļvadi, kas augsts ar augstu spiedienu f. Cauruļvadiem ir nepieciešams skābes izturīgs nerūsējošais tērauds (piemēram, 316L) {. zemas temperatūras izturības tērauds (piemēram, 9% ni tērauds) ir nepieciešams zemas temperatūras videi (piemēram, LNG) . Turklāt, lai nodrošinātu arī drošību un ekonomiku {{{14} {}} {}} {}} {}} {}} {}}} {}} {}} {}} {}} {}} {}}. ir nepieciešams nodrošināt {14}.
Kādas ir grūtības metināšanas nerūsējošā tērauda loka metinātajās caurulēs?
Stainless steel welding is prone to thermal cracking, deformation and intergranular corrosion. Due to its poor thermal conductivity and large thermal expansion coefficient, heat input needs to be controlled to avoid deformation. Carbide precipitation (sensitization) at high temperatures will cause intergranular corrosion, and low-carbon stainless steel (such as 304L) or Metinot, ir jāizvēlas stabilizēts tērauds (piemēram, 321) {., jāizmanto zema strāvas un ātra metināšana, un, lai novērstu oksidāciju ., jāizmanto ar aizmugurējo gāzi (piemēram, argons), var atjaunot korozijas pretestību ..
Vai cinkotās tērauda caurules var tieši sametināt? Kam jāpievērš uzmanība?
Galvanized steel pipes can be directly welded, but the high-temperature volatilization of the zinc layer will produce toxic fumes (zinc vapor), which will endanger the health of welders. Before welding, the zinc layer near the weld should be removed (grinding or pickling), or low smoke electrodes (such as E6013) should be selected. Ventilation should be strengthened during welding and a gas mask should be worn. Zinc vapor may also cause weld porosity, so the welding parameters need to be adjusted (such as slightly higher current). The damaged zinc layer needs to be repaired after welding (such as cold galvanizing paint).
Kāpēc augstas izturības tērauda (piemēram, X80) loka metinātās caurules, ko parasti izmanto naftas un gāzes cauruļvados?
Augstas stiprības tērauds (piemēram, X80) var samazināt cauruļu sienas biezumu, samazināt materiāla izmaksas un transporta svaru, vienlaikus saglabājot augstspiediena pārraides iespējas {. tā ražas stiprums pārsniedz 550MPA, kas ir piemērots tālsatiksmes augstas spiediena eļļai un gāzes pārvadāšanai .. Kontrolēts, lai izvairītos no siltuma skartās zonas . neapmierinātības. Turklāt, lai optimizētu mikrostruktūru un īpašības {.}, šādiem cauruļvadiem ir jāiztur arī stingras lūzuma izturības testi (piemēram, charpy trieciena testi) .}}}}}}}}}}}.} {14} {14} {14} {14} {14} jāiztur arī stingras.